Is 320 Ht2 High Tensile Brass Hollow Bar

High Tensile Brass Hollow Rods / Is 320 Ht2 High Tensile Brass Hollow Bar

IS 320 HT2 High Tensile Brass Hollow Bars are premium high-strength brass alloy bars manufactured to IS 320 standards, offering excellent tensile strength, corrosion resistance, and wear durability. Ideal for marine, heavy engineering, and industrial applications, they provide reliable performance, good machinability, and a long service life in demanding operating conditions.

Download PDF Request a Quote (RFQ)

Urgent Quote? WhatsApp Now

Description
Chemical Composition
Physical Properties

IS 320 HT1 or HT2
BS 2874 CZ114 or CZ115
JIS 3250H C6782 or C6783

IS 320 HT2 High Tensile Brass Hollow Bars are premium high-strength brass alloy bars manufactured to IS 320 standards, offering excellent tensile strength, corrosion resistance, and wear durability. Ideal for marine, heavy engineering, and industrial applications, they provide reliable performance, good machinability, and a long service life in demanding operating conditions.

Chemical Requirements	HT1	HT2
Copper	56.0 - 60.0%	56.0 - 61.0%
Lead	0.20 to 1.50%	0.50 to 1.50%
Iron	0.20 to 1.25%	0.20 to 1.50%
Tin	0.20 to 1.0%	1.0% max
Aluminum	0.2% max	0.30 to 2%
Manganese	0.25 - 2.0%	0.50-2.0%
Total Imp.	0.50% max	0.50% max
Zinc	Remainder	Remainder

Physical Properties
Condition	Size	T.S. MPa	EL% Min	T.S. MPa	EL% Min
As manufactured	All Size	430 min	20%	460 min	20%
Cold-worked & Stress	10-40	480 min	12%	520 min	12%
Relieved	40 above			500 min	15%

Fabrication Properties
Capacity for being
Cold formed	Poor	Fair
Hot worked	Good	Good
Machinability Rating	30%	30%
Resistance to Corrosion	Excellent	Excellent
Suitability for soldering	Excellent	Fair
Uses
HT1 is suitable for Soldering
Ht2 is suitable for Machining